Aging Profiles of AlSi7Mg0.6 and AlSi10Mg0.3 Alloys Manufactured via Laser-Powder Bed Fusion: Direct Aging versus T6

The artificial aging heat treatments performed directly on as-built and solubilized AlSi7Mg0.6 and AlSi10Mg0.3 samples were characterized and discussed. The analysed bars and billets (height of 300 mm) were manufactured via the Laser Powder-Bed Fusion process on a build platform heated at 150 °C. Therefore, its influence on the as-built samples was studied in terms of mechanical performance variations between the bottom and top regions. Vickers microhardness measurements were performed to obtain aging profiles after direct aging (175–225 °C) and T6 heat treatments and to highlight better time and temperature parameters to optimize the mechanical properties of both alloys. SEM observations were used to characterize the microstructure before and after the heat treatments and its influence on the fracture mechanisms. Generally, the direct aging heat treatments show the same effects on both aluminium alloys, unlike the solubilization at 505 °C followed by artificial aging at 175 °C. The strengths vs. elongation values obtained after the direct aging treatments are better than those exhibited by T6 as highlighted by the quality index.