The cast AlSi7Mg alloy prepared using different modifier was studied. The main factor influencing fatigue properties were the casting defects. Using metallography and statistical approach, Larger Extreme Value Distribution (LEVD) theory, the structure and the porosity were evaluated. According to the largest defects sizes prediction fatigue tests were performed. Fatigue cracks were initiated on the casting defects present on the specimen free surface or just below the surface identified using SEM. Specimens fatigue life was influenced by the size of the defect in the initiation place and the number of initiation places. The specimens fatigue behaviour corresponded with the assumptions according to the LEVD.

Microstructure, defects and fatigue behavior of cast AlSi7Mg alloy / Fintová, Stanislava; Konečná, Radomila; Nicoletto, Gianni. - In: ACTA METALLURGICA SLOVACA. - ISSN 1335-1532. - 19:3(2013), pp. 223-231. [10.12776/ams.v19i3.164]

Microstructure, defects and fatigue behavior of cast AlSi7Mg alloy

NICOLETTO, Gianni
2013-01-01

Abstract

The cast AlSi7Mg alloy prepared using different modifier was studied. The main factor influencing fatigue properties were the casting defects. Using metallography and statistical approach, Larger Extreme Value Distribution (LEVD) theory, the structure and the porosity were evaluated. According to the largest defects sizes prediction fatigue tests were performed. Fatigue cracks were initiated on the casting defects present on the specimen free surface or just below the surface identified using SEM. Specimens fatigue life was influenced by the size of the defect in the initiation place and the number of initiation places. The specimens fatigue behaviour corresponded with the assumptions according to the LEVD.
2013
Microstructure, defects and fatigue behavior of cast AlSi7Mg alloy / Fintová, Stanislava; Konečná, Radomila; Nicoletto, Gianni. - In: ACTA METALLURGICA SLOVACA. - ISSN 1335-1532. - 19:3(2013), pp. 223-231. [10.12776/ams.v19i3.164]
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11381/2826026
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 9
  • ???jsp.display-item.citation.isi??? ND
social impact