Nanocrystalline praseodymium doped zirconia powders were produced using a microwave driven hydrothermal process under pressures up to 8 GPa. The aim of the work was to evaluate the effect of synthesis conditions on the phase composition and grain size of nanopowders of zirconia with Pr in solid solutions having Pr contents of: 0, 0.5, 1, 5 and 10 mol %.

Microwave-hydrothermal synthesis of nanocrystalline Pr-doped zirconia powders at pressures up to 8 MPa / Bondioli, Federica; A., Ferrari; S., Braccini; C., Leonelli; G., Pellacani; A., Opalinska; T., Chudoba; E., Grzanka; B., Palosz; W., Lojkowski. - In: DIFFUSION AND DEFECT DATA, SOLID STATE DATA. PART B, SOLID STATE PHENOMENA. - ISSN 1012-0394. - 94:(2003), pp. 193-196.

Microwave-hydrothermal synthesis of nanocrystalline Pr-doped zirconia powders at pressures up to 8 MPa

BONDIOLI, Federica;
2003-01-01

Abstract

Nanocrystalline praseodymium doped zirconia powders were produced using a microwave driven hydrothermal process under pressures up to 8 GPa. The aim of the work was to evaluate the effect of synthesis conditions on the phase composition and grain size of nanopowders of zirconia with Pr in solid solutions having Pr contents of: 0, 0.5, 1, 5 and 10 mol %.
2003
Microwave-hydrothermal synthesis of nanocrystalline Pr-doped zirconia powders at pressures up to 8 MPa / Bondioli, Federica; A., Ferrari; S., Braccini; C., Leonelli; G., Pellacani; A., Opalinska; T., Chudoba; E., Grzanka; B., Palosz; W., Lojkowski. - In: DIFFUSION AND DEFECT DATA, SOLID STATE DATA. PART B, SOLID STATE PHENOMENA. - ISSN 1012-0394. - 94:(2003), pp. 193-196.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11381/2673218
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 22
  • ???jsp.display-item.citation.isi??? 19
social impact