Marble slabs are frequently used as façade panels to externally cover buildings. In some cases bowing of such façade panels after a certain time of environmental exposure is experienced. The bowing is generally accompanied by a progressive reduction of strength. In the present paper, a theoretical model to calculate the progressive bowing and the thermal fatigue of marble slabs submitted to temperature cycles is presented. The model, developed within the framework of fracture mechanics, takes into account the mechanical microstructural characteristics of the marble as well as the actual cyclic temperature field in the material. The slabs are subjected to a thermal gradient along their thickness (due to different values of temperature between the outer and inner sides of the slab) as well as to thermal fluctuation on the two sides of the slab due to daily and seasonal temperature excursions. This thermal action causes a stress field which can locally determine microcracks due to decohesion of calcite grains. Stress intensification near the cracks occurs and leads to crack propagation in the slab. Such crack propagation under thermal actions is evaluated and the corresponding bowing is calculated.

Intergranular Microcracking Due To Anisotropic Thermal Expansion In Calcite Marbles / Spagnoli, Andrea; A. M., Ferrero; M., Migliazza. - (2012). (Intervento presentato al convegno 19th European Conference on Fracture (ECF19) tenutosi a Kazan, Russia nel 26 - 31 August, 2012).

Intergranular Microcracking Due To Anisotropic Thermal Expansion In Calcite Marbles

SPAGNOLI, Andrea;
2012-01-01

Abstract

Marble slabs are frequently used as façade panels to externally cover buildings. In some cases bowing of such façade panels after a certain time of environmental exposure is experienced. The bowing is generally accompanied by a progressive reduction of strength. In the present paper, a theoretical model to calculate the progressive bowing and the thermal fatigue of marble slabs submitted to temperature cycles is presented. The model, developed within the framework of fracture mechanics, takes into account the mechanical microstructural characteristics of the marble as well as the actual cyclic temperature field in the material. The slabs are subjected to a thermal gradient along their thickness (due to different values of temperature between the outer and inner sides of the slab) as well as to thermal fluctuation on the two sides of the slab due to daily and seasonal temperature excursions. This thermal action causes a stress field which can locally determine microcracks due to decohesion of calcite grains. Stress intensification near the cracks occurs and leads to crack propagation in the slab. Such crack propagation under thermal actions is evaluated and the corresponding bowing is calculated.
2012
978-5-905576-18-8
Intergranular Microcracking Due To Anisotropic Thermal Expansion In Calcite Marbles / Spagnoli, Andrea; A. M., Ferrero; M., Migliazza. - (2012). (Intervento presentato al convegno 19th European Conference on Fracture (ECF19) tenutosi a Kazan, Russia nel 26 - 31 August, 2012).
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11381/2435714
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 0
  • ???jsp.display-item.citation.isi??? ND
social impact