Fe/Co multilayers were e-beam evaporated in uhv. Iron thickness was comparable to the domain wall width of bulk iron, and three times that of cobalt. A single-phase magnetic behavior was observed with saturation magnetization comparable to that of iron and coercive force just below that of cobalt film. The squareness of hysteresis loop indicates high homogeneity and low defectivity.
Exchange coupling in nano-metric Fe/Co multilayers / Asti, Giovanni; Carbucicchio, Massimo; M., Rateo; Solzi, Massimo. - In: JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS. - ISSN 0304-8853. - 196:(1999), pp. 59-60. [10.1016/S0304-8853(98)00661-1]
Exchange coupling in nano-metric Fe/Co multilayers
ASTI, Giovanni;CARBUCICCHIO, Massimo;SOLZI, Massimo
1999-01-01
Abstract
Fe/Co multilayers were e-beam evaporated in uhv. Iron thickness was comparable to the domain wall width of bulk iron, and three times that of cobalt. A single-phase magnetic behavior was observed with saturation magnetization comparable to that of iron and coercive force just below that of cobalt film. The squareness of hysteresis loop indicates high homogeneity and low defectivity.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.