Several failures of metallic engineering structures occur due to cyclic loading. The failure process often consists of three stages : (a) crack initiation (from microcrack initiation to engineering-size flaw formation), (b) crack propagation, and (c) final failure. The fatigue phenomena remarkably affect joints and components in the field of the offshore structures. As a matter of fact, these structures are subjected to a severe cyclic loading, and the crack propagation rate is increased by the environmental conditions under which they usually work.
Crack propagation under fatigue loading / Carpinteri, Andrea; Brighenti, Roberto. - (1996), pp. 359-396.
Crack propagation under fatigue loading
CARPINTERI, Andrea;BRIGHENTI, Roberto
1996-01-01
Abstract
Several failures of metallic engineering structures occur due to cyclic loading. The failure process often consists of three stages : (a) crack initiation (from microcrack initiation to engineering-size flaw formation), (b) crack propagation, and (c) final failure. The fatigue phenomena remarkably affect joints and components in the field of the offshore structures. As a matter of fact, these structures are subjected to a severe cyclic loading, and the crack propagation rate is increased by the environmental conditions under which they usually work.File | Dimensione | Formato | |
---|---|---|---|
10_Chapt_Rao.pdf
non disponibili
Tipologia:
Documento in Post-print
Licenza:
NON PUBBLICO - Accesso privato/ristretto
Dimensione
1.75 MB
Formato
Adobe PDF
|
1.75 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.